Cast Iron Electrode Carver - 9750

Additional Details

PROCEDURE
All rust, scale and oil should be removed from the surface to be welded. Preheat casting to 250C and maintain interpass temperature. Maintain a short arc and use either the stringer bead or slight weaving technique. Skip weld in order to dissipate the heat as evenly as possible into the work piece. Peen rapidly to help relieve stresses. Always back-step the crater before breaking the arc. Clean off slag between passes. Cover the finished unit after welding in order to retard the cooling rate.

Technical Specifications

FEATURES
CARVER 9750 is for the repair and joining of heavy sections of cast iron. The high carbon in CARVER 9750 promotes the formation of graphite in the weld metal, thereby reducing shrinkage stresses and the possibility of heat affected zone cracking. CARVER 9750 weld deposits are machinable. Designed specifically for on-the-job repairs of cast iron, which eleminates the necessity of dismantling equipment. While pre-heating is recommended, the electrode may be used without pre-heating or post-heating in many instances.


TECHNICAL DATA
Alloy Type :     Ni, Fe Alloy
Tensile Strength :     430 N/mm2
Machinability :     Good
Hardness :     Rockwell C 21-26

RECOMMENDED CURRENT RANGE
SIZE (mm)     3.15     4.00     5.00
AMPS     90-110     100-130     140-170
 

Applications

APPLICATIONS
Use CARVER 9750 when high strength crack-free welds are required on all cast iron maintenance applications; including motor housings, gears, sprockets, ladles, flaska and trasmission housings, Excellent for building up shy areas and filling holes in castings. Use for all repair and joining welds on gray, malleable, ductile and nodular cast iron and their joining to steel alloys.